SABIC® LLDPE 318BE

线性低密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

Technical Data

 

产品说明

SABIC® LLDPE 318BE is a butene linear low density polyethylene resin designed for easy processing and specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast film produced from SABIC® LLDPE 318BE exhibit excellent optical properties, puncture resistance and tear strength. The suffix E denotes European origin.

 

Applications:

SABIC® LLDPE 318BE resin is recommended for hand and pallet stretch wrap.

 

The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Processing - Cast Film (English)

•  Technical Datasheet (English)

搜索 UL 黄卡 •  Saudi Basic Industries Corporation (SABIC)

供货地区 • 欧洲

添加剂 • 抗氧化性

• 低密度 • 抗氧化性 • 热稳定性，良好

特性 • 光学性能 • 可加工性，良好

• 食品接触的合规性

• 抗穿孔性 • 良好的撕裂强度

用途 • 流延薄膜

形式 • 粒子

加工方法 • 薄膜挤出

 

物理性能 额定值单位制 测试方法

密度 0.918g/cm³ ISO 1183/A

熔流率（熔体流动速率） (190°C/2.16 kg) 2.8g/10 min ISO 1133

薄膜 额定值单位制 测试方法

薄膜厚度 - 经测试 20µm

Elastic Recovery 3 (20.0 µm) 52% ASTM D5459

Protrusion Puncture Resistance 3 (20.0 µm) 2.00J ASTM D5748

Retention Force - 60 sec 3 (20.0 µm) 890g

Stress Retention 3 (20.0 µm) 78% ASTM D5459

Ultimate Pre-stretch Level 3 (20.0 µm) 310%

热性能 额定值单位制 测试方法

维卡软化温度 102°C ISO 306/A

溶融温度（DSC） 121°C 内部方法

光学性能 额定值单位制 测试方法

光泽度 (45°, 20.0 µm, 铸造薄膜) 91 ASTM D2457

雾度 (20.0 µm, 铸造薄膜) 2.1% ASTM D1003

补充信息 额定值单位制 测试方法

Dart Impact 3 (20.0 µm) 26.0J/cm ISO 7765-2

Peel Cling 3 ASTM D5458

0% pre-stretch : 20.0 µm 127.5g/2.5 cm

200% pre-stretch : 20.0 µm 76.5g/2.5 cm

Tear Strength - TD 3 (20.0 µm) 140.0kN/m ISO 6383-2

Film properties

Properties are determined on 20 µm cast stretch film produced on a 2 m commercial cast stretch line: melt temperature 270 °C, chill roll temperature 20 °C and line speed of 450 m/min.

 

Processing conditions

SABIC® LLPDE 318BE is extrudable with conventional cast film extrusion equipment. Minor machine modifications may be required for optimum use. Cast film melt temperatures 250 - 300 °C.

 

 

SABIC® LLDPE 318BE

线性低密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

挤出 额定值单位制

熔体温度 250 到 300°C

 

 

 

 

 

 

 